Microstructure and Performance of Micro CU Pillars Assemblies

Authors: Mohammed Genanu ¹, Babak Arfaei, Ph.D.5, Eric J.Cotts, Ph.D.¹, Francis Mutuku ², Eric Perfecto ³, Scott Pollard 4, Aric Shorey 4
Company: ¹ Physics and Materials Science Binghamton University, ² Universal Instruments Corporation, ³ IBM Corporation (now GlobalFoundries), 4 Corning Inc., 5 Ford Motor Company
Date Published: 9/25/2016   Conference: SMTA International


Abstract: The desire for smaller, lighter and faster products drives the development of 2.5D/3D integration technologies that can utilize tens of thousands of connections per die. Micro copper (Cu) pillar geometries have been widely adopted because their small size and fine pitch provides high thermal conductivity, higher input/output (I/O) density and resistance to deleterious electromigration effects. In micro Cu-pillars, SnAg solder is electroplated on top of a Cu pillar. Because of the small volume of solder employed, intermetallic compounds comprise a significant fraction of the resulting solder joint, and very fine Ag3Sn precipitate morphologies can occur. Thus, the microstructure of SnAg solder/Cu pillar microstructures varies significantly from that of larger solder joints such as flip chip solder joints. Furthermore, 2.5D applications include interposers of distinctly different materials, such as Si or glass. The different properties of these materials such as coefficient of thermal expansion, affect the thermomechanical response of the package to temperature excursions and the lifetime of the package. Thus, behaviors of Cu pillar packages during Accelerated Thermal Cycling (ATC) were examined. Correlations between the shear strength and microstructure of Cu pillars were examined for different solder compositions, and for different aging times. Microstructure analysis (e.g. Ag3Sn precipitate morphology) was performed with both optical and scanning electron microscopy. The effects of thermal aging on the growth of intermetallic compounds (IMCs), the Ag3Sn precipitate morphology and on the mechanical properties of micro Cu pillar bumps were examined. The shear strength performance of micro Cu pillars with three different bump diameters (30µm, 50µm, and 100µm) was also evaluated. Results were considered in terms of variations in the precipitate morphology, and in terms of increases in the thicknesses of intermetallic layers at micro solder/substrate interfaces. ATC test results for two different interposers (Si and Glass with High CTE) will be discussed.

Key Words: 

Cu Pillars, Lead-Free Solder Alloys, 2.5D Packaging, Interposers, Shear Strength



Members download articles for free:

Not a member yet?

What else do you get when you join SMTA? Read about all of the benefits that go along with membership.

Notice: Sharing of articles is restricted to just your immediate work group. Downloaded papers should not be stored on an external network or shared on the internet.


Back


SMTA Headquarters
6600 City West Parkway, Suite 300
Eden Prairie, MN 55344 USA

Phone +1 952.920.7682
Fax +1 952.926.1819