EFFECT OF TEMPERATURE CYCLING PARAMETERS ON THE SOLDER JOINT RELIABILITY OF A Pb-FREE PBGA PACKAGEAuthors: John Manock, Richard Coyle, Brian Vaccaro, Heather McCormick, Richard Popowich, Debra Fleming, Peter Read, John Osenbach, and Dan Gerlach
Company: Alcatel-Lucent, LSI Corp., and Celestica Inc.
Date Published: 10/11/2007 Conference: SMTA International
In the current study, multiple temperature cycling conditions are used to extend the evaluation of SAC solder joint reliability and aid in the development of fatigue life modeling capability necessary for the determination of test acceleration factors. To address the ongoing controversy of accumulated creep damage during temperature cycling, the 0°C to 100°C test was conducted using both 30 minute and 60 minute dwell times and the results compared to the previous study that used 10 minute dwells. An additional 30 minute dwell test cell was performed with samples isothermally preconditioned for 500 hours at 125°C to assess potential microstructural effects due to storage prior to use. To explore the effect of different temperature extremes and temperature range, another test was conducted using -40°C to 125°C test conditions. All cells were tested to 63.2% or greater failure rate with a test duration exceeding 4000 cycles. Complete analysis of the test data for each cell is presented.
Post-cycling failure analysis was conducted on representative test samples from each cell. Failure analyses include dye-and-pry analysis to determine the location of the failed joints within a test net, metallographic analyses using optical and polarized light microscopy (PLM), and scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS) to verify the failure mode and evaluate the microstructure. The ATC test data and failure analysis results are discussed in terms of the relationship to the evolving microstructure and mechanical behavior that results from temperature cycling and preconditioning.
Key words: Lead Free, PBGA, Temperature Cycling, Reliability, dwell time, Pb free, microstructure
Members download articles for free:
Not a member yet?
What else do you get when you join SMTA? Read about all of the benefits that go along with membership.
Notice: Sharing of articles is restricted to just your immediate work group. Downloaded papers should not be stored on an external network or shared on the internet.