The Risk and Solution for No-Clean Flux Not Fully Dried under Component Terminations

Authors: Fen Chen and Ning Cheng Lee, Ph.D.
Company: Indium Corporation
Date Published: 9/27/2015   Conference: SMTA International


Abstract: The miniaturization trend is driving industry to adopting low standoff components or components in cavity. The cost reduction pressure is pushing telecommunication industry to combine assembly of components and electromagnetic shield in one single reflow process. As a result, the flux outgassing/drying is getting very difficult for devices due to poor venting channel. This resulted in insufficiently dried/burnt-off flux residue. For a properly formulated flux, the remaining flux activity posed no issue in a dried flux residue for no-clean process. However, when venting channel is blocked, not only solvents remain, but also activators could not be burnt off. The presence of solvents allows mobility of active ingredients and the associated corrosion, thus poses a major threat to the reliability. In this work, a new halogen-free no-clean SnAgCu solder paste, 33-76-1, has been developed. This solder paste exhibited SIR value above the IPC spec 100 MO without any dendrite formation, even with a wet flux residue on the comb pattern. The wet flux residue was caused by covering the comb pattern with 10 mm × 10 mm glass slide during reflow and SIR testing in order to mimic the poorly vented low standoff components. The paste 33-76-1 also showed very good SMT assembly performance, including voiding of QFN and HIP resistance. The wetting ability of paste 33-76-1 was very good under nitrogen. For air reflow, 33-76-1 still matched paste C which is widely accepted by industry for air reflow process. The above good performance on both non-corrosivity with wet flux residue and robust SMT process can only be accomplished through a breakthrough in flux technology.

Key Words: 

No-clean, flux, Surface Insulation Resistance (SIR), SAC305, halogen-free, soldering, low standoff components, wet flux residue



Cost to download:

  Members: Free! (Log on to receive the member rate)
  Non-Members: $10

Why become an SMTA member?

Not a member yet? Join SMTA today!

Notice: Sharing of articles is prohibited. Downloaded papers must only be stored on a local hard drive and not in a shared repository either internal or external.


Back


SMTA Headquarters
6600 City West Parkway, Suite 300
Eden Prairie, MN 55344

Phone 952.920.7682
Fax 952.926.1819
Home
Site Map
Update Your Info
Related Links
Send Us Feedback
Contact Us
Privacy Policy
↑ Top